dupont performance polymers zytel® 135f nc010 nylon 66 (unverified data**) 物性表
機(jī)械性能
額定值 (公制)
額定值 (英制)
測(cè)試方法
|
洛氏硬度（m 級(jí)）
|
64
|
64
|
50％rh; iso 2039-2
|
|
|
87
|
87
|
dam; iso 2039-2
|
|
洛氏硬度（r 級(jí)）
|
116
|
116
|
50％rh; iso 2039-2
|
|
|
123
|
123
|
dam; iso 2039-2
|
|
抗張強(qiáng)度
|
7.47 mpa
@strain 0.960 ％, temperature 90.0 °c
|
1080 psi
@strain 0.960 ％, temperature 194 °f
|
dam; iso 11403-1 -2
|
|
|
11.4 mpa
@strain 0.480 ％, temperature 40.0 °c
|
1650 psi
@strain 0.480 ％, temperature 104 °f
|
dam; iso 11403-1 -2
|
|
|
17.8 mpa
@strain 2.40 ％, temperature 90.0 °c
|
2580 psi
@strain 2.40 ％, temperature 194 °f
|
dam; iso 11403-1 -2
|
|
|
18.0 mpa
@strain 0.480 ％, temperature 23.0 °c
|
2610 psi
@strain 0.480 ％, temperature 73.4 °f
|
dam; iso 11403-1 -2
|
|
|
22.8 mpa
@strain 0.550 ％, temperature 0.000 °c
|
3310 psi
@strain 0.550 ％, temperature 32.0 °f
|
dam; iso 11403-1 -2
|
|
|
24.5 mpa
@strain 3.84 ％, temperature 90.0 °c
|
3550 psi
@strain 3.84 ％, temperature 194 °f
|
dam; iso 11403-1 -2
|
|
|
26.5 mpa
@strain 0.630 ％, temperature -20.0 °c
|
3840 psi
@strain 0.630 ％, temperature -4.00 °f
|
dam; iso 11403-1 -2
|
|
|
41.6 mpa
@strain 1.92 ％, temperature 40.0 °c
|
6030 psi
@strain 1.92 ％, temperature 104 °f
|
dam; iso 11403-1 -2
|
|
|
60.5 mpa
@strain 3.36 ％, temperature 40.0 °c
|
8770 psi
@strain 3.36 ％, temperature 104 °f
|
dam; iso 11403-1 -2
|
|
|
65.5 mpa
@strain 1.92 ％, temperature 23.0 °c
|
9500 psi
@strain 1.92 ％, temperature 73.4 °f
|
dam; iso 11403-1 -2
|
|
|
65.7 mpa
@strain 4.80 ％, temperature 40.0 °c
|
9530 psi
@strain 4.80 ％, temperature 104 °f
|
dam; iso 11403-1 -2
|
|
|
82.7 mpa
@strain 2.20 ％, temperature 0.000 °c
|
12000 psi
@strain 2.20 ％, temperature 32.0 °f
|
dam; iso 11403-1 -2
|
|
|
92.9 mpa
@strain 3.36 ％, temperature 23.0 °c
|
13500 psi
@strain 3.36 ％, temperature 73.4 °f
|
dam; iso 11403-1 -2
|
|
|
95.4 mpa
@strain 2.52 ％, temperature -20.0 °c
|
13800 psi
@strain 2.52 ％, temperature -4.00 °f
|
dam; iso 11403-1 -2
|
|
|
117 mpa
@strain 3.85 ％, temperature 0.000 °c
|
17000 psi
@strain 3.85 ％, temperature 32.0 °f
|
dam; iso 11403-1 -2
|
|
|
133 mpa
@strain 4.41 ％, temperature -20.0 °c
|
19300 psi
@strain 4.41 ％, temperature -4.00 °f
|
dam; iso 11403-1 -2
|
|
|
3.00 mpa
@strain 0.165 ％, time 36000 sec
|
435 psi
@strain 0.165 ％, time 10.0 hour
|
50％rh; isochronous; iso 11403-1 -2
|
|
|
3.00 mpa
@strain 0.192 ％, time 360000 sec
|
435 psi
@strain 0.192 ％, time 100 hour
|
50％rh; isochronous; iso 11403-1 -2
|
|
|
3.00 mpa
@strain 0.231 ％, time 3.60e+6 sec
|
435 psi
@strain 0.231 ％, time 1000 hour
|
50％rh; isochronous; iso 11403-1 -2
|
|
|
3.00 mpa
@strain 0.146 ％, time 3600 sec
|
435 psi
@strain 0.146 ％, time 1.00 hour
|
50％rh; isochronous; iso 11403-1 -2
|
|
|
3.00 mpa
@strain 0.297 ％, time 3.60e+7 sec
|
435 psi
@strain 0.297 ％, time 10000 hour
|
50％rh; isochronous; iso 11403-1 -2
|
|
|
12.0 mpa
@strain 1.45 ％, time 3.60e+7 sec
|
1740 psi
@strain 1.45 ％, time 10000 hour
|
50％rh; isochronous; iso 11403-1 -2
|
|
|
12.0 mpa
@strain 0.656 ％, time 3600 sec
|
1740 psi
@strain 0.656 ％, time 1.00 hour
|
50％rh; isochronous; iso 11403-1 -2
|
|
|
12.0 mpa
@strain 1.18 ％, time 3.60e+6 sec
|
1740 psi
@strain 1.18 ％, time 1000 hour
|
50％rh; isochronous; iso 11403-1 -2
|
|
|
12.0 mpa
@strain 0.947 ％, time 360000 sec
|
1740 psi
@strain 0.947 ％, time 100 hour
|
50％rh; isochronous; iso 11403-1 -2
|
|
|
12.0 mpa
@strain 0.772 ％, time 36000 sec
|
1740 psi
@strain 0.772 ％, time 10.0 hour
|
50％rh; isochronous; iso 11403-1 -2
|
|
抗張強(qiáng)度(屈服)
|
67.0 mpa
|
9720 psi
|
50％rh; iso 527-1/-2
|
|
|
96.0 mpa
|
13900 psi
|
dam; iso 527-1/-2
|
|
伸長率 (斷裂)
|
13 ％
|
13 ％
|
dam; nominal; iso 527-1/-2
|
|
|
50 ％
|
50 ％
|
50％rh; nominal; iso 527-1/-2
|
|
屈服伸長率
|
4.5 ％
|
4.5 ％
|
dam; iso 527-1/-2
|
|
|
4.5 ％
|
4.5 ％
|
dam; iso 527-3
|
|
|
18 ％
|
18 ％
|
50％rh; iso 527-1/-2
|
|
拉伸模量
|
2.00 gpa
|
290 ksi
|
50％rh; iso 527-1/-2
|
|
|
3.60 gpa
|
522 ksi
|
dam; iso 527-1/-2
|
|
剪切模量
|
0.175 gpa
@temperature 160 °c
|
25.4 ksi
@temperature 320 °f
|
dam; dynamic; iso 11403-1 -2
|
|
|
0.214 gpa
@temperature 120 °c
|
31.0 ksi
@temperature 248 °f
|
dam; dynamic; iso 11403-1 -2
|
|
|
0.449 gpa
@temperature 70.0 °c
|
65.1 ksi
@temperature 158 °f
|
dam; dynamic; iso 11403-1 -2
|
|
|
1.0685 gpa
@temperature 20.0 °c
|
154.98 ksi
@temperature 68.0 °f
|
dam; dynamic; iso 11403-1 -2
|
|
|
1.171 gpa
@temperature -20.0 °c
|
169.8 ksi
@temperature -4.00 °f
|
dam; dynamic; iso 11403-1 -2
|
|
|
1.259 gpa
@temperature -50.0 °c
|
182.6 ksi
@temperature -58.0 °f
|
dam; dynamic; iso 11403-1 -2
|
|
抗剪強(qiáng)度
|
0.0670 mpa
@shear rate 500 1/s, temperature 315 °c
|
9.72 psi
@shear rate 500 1/s, temperature 599 °f
|
iso 11403-1 -2
|
|
|
0.0975 mpa
@shear rate 500 1/s, temperature 295 °c
|
14.1 psi
@shear rate 500 1/s, temperature 563 °f
|
iso 11403-1 -2
|
|
|
0.142 mpa
@shear rate 500 1/s, temperature 275 °c
|
20.6 psi
@shear rate 500 1/s, temperature 527 °f
|
iso 11403-1 -2
|
|
割線模量
|
1.66 gpa
@strain 3.84 ％, temperature 40.0 °c
|
240 ksi
@strain 3.84 ％, temperature 104 °f
|
dam; iso 11403-1 -2
|
|
|
2.17 gpa
@strain 1.92 ％, temperature 40.0 °c
|
314 ksi
@strain 1.92 ％, temperature 104 °f
|
dam; iso 11403-1 -2
|
|
|
2.375 gpa
@strain 0.480 ％, temperature 40.0 °c
|
344.5 ksi
@strain 0.480 ％, temperature 104 °f
|
dam; iso 11403-1 -2
|
|
|
2.52 gpa
@strain 3.84 ％, temperature 23.0 °c
|
365 ksi
@strain 3.84 ％, temperature 73.4 °f
|
dam; iso 11403-1 -2
|
|
|
2.7381 gpa
@strain 5.04 ％, temperature -20.0 °c
|
397.13 ksi
@strain 5.04 ％, temperature -4.00 °f
|
dam; iso 11403-1 -2
|
|
|
2.77 gpa
@strain 4.40 ％, temperature 0.000 °c
|
402 ksi
@strain 4.40 ％, temperature 32.0 °f
|
dam; iso 11403-1 -2
|
|
|
3.41 gpa
@strain 1.92 ％, temperature 23.0 °c
|
495 ksi
@strain 1.92 ％, temperature 73.4 °f
|